HEAL DSpace

Διερεύνηση λειτουργίας και βελτιστοποίηση κυκλώματος θραύσης μεταλλεύματος ΛΑΡΚΟ

Αποθετήριο DSpace/Manakin

Εμφάνιση απλής εγγραφής

dc.contributor.author Παπακωνσταντίνου, Ρεβέκκα el
dc.contributor.author Papakonstantinou, Revekka en
dc.date.accessioned 2018-12-04T09:40:13Z
dc.date.available 2018-12-04T09:40:13Z
dc.date.issued 2018-12-04
dc.identifier.uri https://dspace.lib.ntua.gr/xmlui/handle/123456789/48192
dc.identifier.uri http://dx.doi.org/10.26240/heal.ntua.16053
dc.rights Αναφορά Δημιουργού-Μη Εμπορική Χρήση-Όχι Παράγωγα Έργα 3.0 Ελλάδα *
dc.rights.uri http://creativecommons.org/licenses/by-nc-nd/3.0/gr/ *
dc.subject Μηχανική προπαρασκευή el
dc.subject Θραυστήρας σιαγόνων el
dc.subject Κωνικός θραυστήρας (θραύσης-ταξινόμησης) el
dc.subject ΛΑΡΚΟ el
dc.title Διερεύνηση λειτουργίας και βελτιστοποίηση κυκλώματος θραύσης μεταλλεύματος ΛΑΡΚΟ el
heal.type bachelorThesis
heal.classification Μηχανική προπαρασκευή (θραύση-ταξινόμηση) el
heal.language el
heal.access free
heal.recordProvider ntua el
heal.publicationDate 2018-10-16
heal.abstract Στο πλαίσιο της παρούσας διπλωματικής εργασίας ασχολήθηκα με την μηχανική προπαρασκευή (Θραύση-Ταξινόμηση) του μεταλλεύματος της ΛΑΡΚΟ, που είναι το στάδιο προετοιμασίας του υλικού πριν την εισαγωγή του στις περιστροφικές καμίνους. Συγκεκριμένα, δείγμα λατερίτη 25kg, που στάλθηκε από τον Αγ. Ιωάννη Βοιωτίας εξετάστηκε στο Εργαστήριο Εμπλουτισμού Μεταλλευμάτων. Σε αυτό διενεργήθηκε πρωτογενής θραύση σε θραυστήρα σιαγόνων και στη συνέχεια το προϊόν υποβλήθηκε σε μηχανική κοσκίνιση (ταξινόμηση του προϊόντος σε κόσκινα μικρότερα από 20mm) και προσδιορίστηκε το ποσοστό υγρασίας του. Από το διάγραμμα κοκκομετρικής ανάλυσης Gates-Gaudin-Schuhmann διαπιστώνεται ότι το μετάλλευμα είναι εύθρυπτο αλλά, λόγω του σημαντικού ποσοστού υγρασίας που περιέχει, χρειάζεται προσοχή κατά την προετοιμασία για να αποκτήσει κατάλληλη κοκκομετρία για την τροφοδοσία στις περιστροφικές καμίνους. Από την άλλη στο «τριβείο» του Αγ. Ιωάννη το μέγιστο μέγεθος του λατερίτη που εισάγεται στο σιλό του τριβείου είναι περίπου 30cm. Χρησιμοποιώντας διαγράμματα και πίνακες της Metso Minerals για θραυστήρες σιαγόνων και κωνικούς, καθώς έχοντας γνωστά δεδομένα του λατερίτη της ΛΑΡΚΟ υπολογίστηκαν για διάφορα ανοίγματα πλέγματος κοσκίνου (συγκεκριμένα 10mm, 15mm, 20mm) οι δυναμικότητες των διαφόρων θραυστήρων και οι αντίστοιχες επιφάνειες κοσκίνισης για τροφοδοσία 100t/h. Τα αποτελέσματα που προέκυψαν μπορούν εύκολα να αναχθούν στις απαιτήσεις δυναμικότητας του κυκλώματος θραύσης-ταξινόμησης, λαμβάνοντας υπόψη την τρέχουσα παραγωγική δυναμικότητα σε Fe-Ni (t/year) του μεταλλουργικού εργοστασίου. el
heal.abstract The present diploma thesis deals with the mechanical preparation (crushing-sizing procedure) of the lateritic nickel ore (LARCO), which is necessary for the preparation of the ore prior to its feeding to the rotary kilns. Specifically, a sample of 25kg ore from Agios Ioannis mine, was delivered to the Laboratory of Mineral Processing. The whole sample was mechanically processed at the Laboratory. Initially, the sample was subjected to primary (jaw crusher) and secondary crushing (cone crushing). Afterwards, the product of the crushing procedure, was sized to various size fractions finer than 20mm, which is the upper size of the kiln feed. From the Gates-Gaudin-Schuhmann (G-G-S) graph produced from the size analysis procedure, it was found that the ore is relatively soft but, due to its considerable moisture content, specific care must be paid during its mechanical preparation to obtain the appropriate particle size distribution for feeding the rotary kilns. On the other hand, knowing that the maximum size of lateritic ore fed to the crushing plant is about 30cm, a suitable crushing/sizing flowsheet was studied and designed in order to produce the appropriate size analysis of the kiln feed from the above mentioned ore. Using Metso Minerals diagrams and tables for jaw and cone crushers, as well as the LARCO lateritic ore size analysis data (ore extracted and target product), the capacities of the various crushers and their respective sieving surfaces were calculated for various mesh openings (10mm, 15mm, 20mm) for a capacity of 100t/h. The results obtained from the above procedure can be easily extrapolated to the actual capacity requirements of the crushing/sizing circuit, taking into account the annual production capacity (t/year) of the metallurgical plant in ferronickel (Fe-Ni) alloy. en
heal.advisorName Τσακαλάκης, Κωνσταντίνος el
heal.committeeMemberName Τσακαλάκης, Κωνσταντίνος el
heal.committeeMemberName Αναστασάκης, Γεώργιος el
heal.committeeMemberName Ξενίδης, Άνθιμος el
heal.academicPublisher Εθνικό Μετσόβιο Πολυτεχνείο. Σχολή Μηχανικών Μεταλλείων Μεταλλουργών. Τομέας Μεταλλουργίας και Τεχνολογίας Υλικών. Εργαστήριο Εμπλουτισμού των Μεταλλευμάτων el
heal.academicPublisherID ntua
heal.numberOfPages 76 σ.
heal.fullTextAvailability true


Αρχεία σε αυτό το τεκμήριο

Οι παρακάτω άδειες σχετίζονται με αυτό το τεκμήριο:

Αυτό το τεκμήριο εμφανίζεται στην ακόλουθη συλλογή(ές)

Εμφάνιση απλής εγγραφής

Αναφορά Δημιουργού-Μη Εμπορική Χρήση-Όχι Παράγωγα Έργα 3.0 Ελλάδα Εκτός από όπου ορίζεται κάτι διαφορετικό, αυτή η άδεια περιγράφεται ως Αναφορά Δημιουργού-Μη Εμπορική Χρήση-Όχι Παράγωγα Έργα 3.0 Ελλάδα