Αξιολόγηση της επιδεκτικότητας κοίλανσης αλουμινίου AA3003 με μικροδομή προερχόμενη από συνεχή-χύτευση-σε-έλασμα (Twin Roll Casting) ή κατόπιν χύτευσης σε πλίνθωμα(Direct Casting) και θερμής έλασης

Εξάρχου, Στέλλα-Μαρία; Exarchou, Stella-Maria

dc.contributor.author	Εξάρχου, Στέλλα-Μαρία	el
dc.contributor.author	Exarchou, Stella-Maria	en
dc.date.accessioned	2019-03-20T12:53:22Z
dc.date.available	2019-03-20T12:53:22Z
dc.date.issued	2019-03-20
dc.identifier.uri	https://dspace.lib.ntua.gr/xmlui/handle/123456789/48487
dc.identifier.uri	http://dx.doi.org/10.26240/heal.ntua.16454
dc.rights	Default License
dc.subject	Texture	en
dc.title	Αξιολόγηση της επιδεκτικότητας κοίλανσης αλουμινίου AA3003 με μικροδομή προερχόμενη από συνεχή-χύτευση-σε-έλασμα (Twin Roll Casting) ή κατόπιν χύτευσης σε πλίνθωμα(Direct Casting) και θερμής έλασης	el
dc.title	Evaluation of texture of Al-Mn sheets produced by CC and DC casting	en
heal.type	bachelorThesis
heal.classification	Engineering	el
heal.language	el
heal.access	free
heal.recordProvider	ntua	el
heal.publicationDate	2018-10-01
heal.abstract	Η παρούσα εργασία μελετά την εξέλιξη του κρυσταλλογραφικού ιστού φύλλων θερμής και ψυχρής έλασης αλουμινίου ΑΑ3003, προερχόμενα από δύο διαφορετικές μεθόδους χύτευσης, την συνεχή (Twin Roll Casting) και την ημισυνεχή (Direct Casting). Συγκεκριμένα, εξετάστηκαν δείγματα προερχόμενα από TRC, φύλλα θερμής έλασης, καθώς και φύλλα ψυχρής έλασης των δύο μεθόδων χύτευσης. Τα φύλλα ψυχρής έλασης υποβλήθηκαν σε θερμική κατεργασία στους 450oC, 500oC και 550oC για 5 λεπτά. Στόχος της μελέτης είναι η αξιολόγηση και η σύγκριση της συμπεριφοράς διαμόρφωσης των φύλλων σε βαθιά κοίλανση, έπειτα από ψυχρή έλαση κι ανόπτηση. Από τα αποτελέσματα που προέκυψαν, τα δείγματα των διαφορετικών μεθόδων χύτευσης, συγκρίθηκαν ως προς τη μορφολογία των κόκκων,την ανισοτροπία και τον κρυσταλλογραφικό ιστό. Παρατηρήθηκαν σημαντικές διαφορές στη μορφολογία και το μέγεθος των κόκκων σε όλες τις εξεταζόμενες καταστάσεις. Οι δοκιμές εφελκυσμού και βαθιάς κοίλανσης διεξήχθησαν σε φύλλα ψυχρής έλασης TRC και DC, πριν και μετά από θερμική κατεργασία. Η ανισοτροπία των φύλλων βελτιώθηκε σημαντικά μετά την ανόπτηση. Από την αξιολόγηση του κρυσταλλογραφικού ιστού το ανοπτημένο δείγμα DC παρουσίασε ένα ισορροπημένο συνδυασμό συστατικού κύβου και άλλων συστατικών του κρυσταλλογραφικού ιστού. Επομένως εμφάνισε καλύτερη συμπεριφορά διαμόρφωσης από το δείγμα TRC.	el
heal.abstract	This study explores the evolution of texture in sh eets of alumi num alloy AA3003 produced by two casting technologies, Twin Roll Castin g and Direct Chill Casting. More specifically, strips produced by TRC and hot rolling processes were examined, as well as cold rolled sheets of the two casting methods. The cold rolled sheets were heat treated at 450 o C,500 o C and 550 o C for 5 minutes. The aim of this study was to evaluate and compare the different formability behavior, of cold rolled and annealed sheets from these casting processes. From the results obtained, the samples of the different casting methods were compared by grain size and morphology, anisotropy and crystallographic texture. Significant differences in the grain structure and size were observed in all the tested specimens . Tensile, and earing cup tes ts were conducted on the TRC and DC cold rolled sheets before and after heat treatment. The mechanical isotropy of both TRC and DC sheets was significantly improved after annealing. Electron backscatter diffraction (EBSD) technique was used for texture evaluation. The annealed DC sample presented a balanced mixture of cube and other texture components exhibiting less anisotropy and therefore exhibited better formability behavior than TRC sample	en
heal.sponsor	This study explores the evolution of texture in sheets of aluminum alloy AA3003 produced by two casting technologies, Twin Roll Casting and Direct Chill Casting. More specifically, strips produced by TRC and hot rolling processes were examined, as well as cold rolled sheets of the two casting methods. The cold rolled sheets were heat treated at 450oC,500oC and 550oC for 5 minutes. The aim of this study was to evaluate and compare the different formability behavior, of cold rolled and annealed sheets from these casting processes. From the results obtained, the samples of the different casting methods were compared by grain size and morphology, anisotropy and crystallographic texture. Significant differences in the grain structure and size were observed in all the tested specimens. Tensile, and earing cup tests were conducted on the TRC and DC cold rolled sheets before and after heat treatment. The mechanical isotropy of both TRC and DC sheets was significantly improved after annealing. Electron backscatter diffraction (EBSD) technique was used for texture evaluation. The annealed DC sample presented a balanced mixture of cube and other texture components exhibiting less anisotropy and therefore exhibited better formability behavior than TRC sample.	en
heal.advisorName	Παπαευθυμίου, Σπύρος	el
heal.committeeMemberName	Φούρλαρης, Γεώργιος	el
heal.committeeMemberName	Παπαευθυμίου, Σπύρος	el
heal.committeeMemberName	Ξενίδης, Άνθιμος	el
heal.academicPublisher	Εθνικό Μετσόβιο Πολυτεχνείο. Σχολή Μηχανικών Μεταλλείων Μεταλλουργών. Τομέας Μεταλλουργίας και Τεχνολογίας Υλικών. Εργαστήριο Μεταλλογνωσίας	el
heal.academicPublisherID	ntua
heal.numberOfPages	87 σ.
heal.fullTextAvailability	true